ABSTRACT

A point chisel includes a substantially cylindrical shank and a working end region that tapers to a point. The working end region has at least three converging substantially planar surfaces, each with a protruding elongate rib extending along at least part of its length. Adjacent surfaces meet along at least part of their length at substantially straight edges between adjacent ribs. A flat chisel includes a substantially cylindrical shank and a working end region with a pair of converging substantially planar surfaces that include a plurality of protruding elongate ribs extending along at least part of its length. Each rib has, along the majority of its length, a substantially constant height above the surface from which it protrudes. Each chisel is made from steel, with the shank having a bainitic microstructure and the working end region having a martensitic microstructure.

RELATED APPLICATIONS

The present application claims priority under 35 U.S.C. §119(e) to U.S. Provisional Patent Application No. 61/466,228, filed Mar. 22, 2011, titled “Chisels,” which is incorporated by reference.

TECHNICAL FIELD

The present application relates to chisels, especially to chisel bits for attachment to powered hammer drills or powered rotary hammers.

SUMMARY

The present application seeks to provide improved chisel shapes and materials, and also to provide an improved process of producing chisels.

According to a first aspect, a point chisel includes a substantially circular cross-section shank having a longitudinal axis and including a tapered working end region in which the shank tapers to a working point, the tapered working end region comprising at least three converging substantially planar ribbed surfaces, each of which includes an elongate rib protruding therefrom and extending along at least part of the length thereof, wherein adjacent ribbed surfaces meet each other along at least part of their length at a substantially straight edge region situated between adjacent elongate ribs.

Embodiments of this aspect may include one or more of the following features. Each substantially straight edge region may project radially outwardly with respect to the longitudinal axis. Each substantially straight edge region may be rounded in cross-section along at least part of its length. The tapered working end region may include a working point region situated between the ribbed surfaces and the working point, the working point region comprising at least three converging substantially planar non-ribbed surfaces which meet at the working point. Each non-ribbed surface may extend from a respective ribbed surface but is not coplanar therewith. The non-ribbed surfaces may converge at a greater angle than do the ribbed surfaces. Each rib may include a front end surface substantially coplanar with, and extending into, a respective non-ribbed surface of the working point region.

Each rib may have longitudinally extending substantially parallel and substantially planar side walls. Each rib may have a substantially constant width along its length. Each rib may vary in height along its length, above its respective ribbed surface. For example, each rib may include an apex situated part way along its length. The point chisel may include at least four, e.g., exactly four, converging substantially planar ribbed surfaces. There may be the same number of non-ribbed surfaces as ribbed surfaces.

According to a second aspect, a flat chisel has a working edge, the chisel comprising a substantially cylindrical shank having a longitudinal axis and including a working end region comprising a pair of converging substantially planar ribbed surfaces on opposite sides of the longitudinal axis, each of which extends directly from a cylindrical surface of the shank and includes a plurality of elongate ribs protruding therefrom and extending along at least part of the length thereof, each rib having, along the majority of its length, a substantially constant height above the surface from which it protrudes.

Embodiments of this aspect may include one or more of the following features. The ribs of each ribbed surface of the flat chisel may be substantially parallel to each other, and may be substantially parallel to a plane that extends through the longitudinal axis and perpendicular to the ribbed surfaces. Each ribbed surface of the flat chisel may have at least three, e.g., exactly three, ribs. At least one of the ribs of each ribbed surface may be longer than the other rib or ribs. For example, a middle rib may be longer than the ribs situated on each side of it. Each rib of the flat chisel may have a substantially constant width along its length. Each rib of the flat chisel may have generally flat side walls and/or a substantially flat upper surface. The substantially flat upper surface may be substantially parallel to the surface from which the rib protrudes.

The working end region of the flat chisel may include a widened portion which is wider than the cylindrical shank, and which extends to the working edge. Two of the ribs of each ribbed surface may extend along, or adjacent to, opposite lateral edges of the widened portion. Respective side walls of two of the ribs of each ribbed surface may form part of opposite lateral surfaces defining the opposite lateral edges of the widened portion.

The working end region of the flat chisel may include a working edge region situated between the ribbed surfaces and the working edge, the working edge region comprising a pair of converging substantially planar non-ribbed surfaces, each of which extends from a respective ribbed surface, which non-ribbed surfaces meet at the working edge. Each non-ribbed surface may be non-coplanar with the ribbed surface from which it extends. The non-ribbed surfaces may converge at a greater angle than do the ribbed surfaces. Each rib may include a front end surface substantially coplanar with, and extending into, a respective non-ribbed surface of the working edge region.

According to a third aspect, a steel chisel comprises an elongate shank having a longitudinal axis, and a working end region, wherein the steel of the shank has a microstructure comprising bainite, and the steel of the working end region has a microstructure comprising martensite.

Embodiments of this aspect may include one or more of the following features. The shank and the working end region may be welded together, e.g., friction welded together. The steel of the working end region may be selected from the group consisting of: S7; 1.2357 50CrMoV 13-14; 1.2542 45WCrV7; and 1.2362×63CrMoV 5-1. The steel of the shank may be selected from the group consisting of: 1.6582 34CrNiMo6; and 1.2249 45SiCrV6. The chisel may comprise a point chisel wherein the working end region includes a working point. For example, the chisel may comprise a point chisel according to the first aspect of the invention. Alternatively, the chisel may comprise a flat chisel wherein the working end region includes a working edge. For example, the chisel may comprise a flat chisel according to the second aspect of the invention.

According to a fourth aspect, a process of producing a steel chisel, comprises:

-   -   (a) providing a shank portion of the chisel formed from a first         steel composition;     -   (b) providing a working end portion of the chisel formed from a         second steel composition, the second steel composition being         different to the first steel composition;     -   (c) joining together the shank portion and the working end         portion;     -   (d) heating the joined shank and working end portions such that         they both have a microstructure comprising austenite; and     -   (e) cooling the heated joined shank and working end portions         such that the first steel composition of the shank portion         adopts a microstructure comprising bainite and such that the         second steel composition of the working end portion adopts a         microstructure comprising martensite.

Embodiments of this aspect may include one or more of the following features. Step (c) of the process according to the fourth aspect of the invention may include welding together the shank portion and the working end portion, e.g., by friction welding together the shank portion and the working end portion. Step (d) of the process may include heating the joined shank and working end portions to a temperature of at least 730 degrees Celsius, e.g., at least 750 degrees Celsius, at least 850 degrees Celsius, at least 950 degrees Celsius, or at least 1050 degrees Celsius. The joined shank and working end portions may be heated to a temperature no greater than 1200 degrees Celsius, e.g., no greater than 1100 degrees Celsius. The heating of step (d) may be carried out for at least 8 minutes, e.g., for at least 12 minutes, or for approximately 17.5 minutes.

Step (e) of the process may include quenching (quench cooling), e.g., gas quenching, the joined shank and working end portions. The quench gas may comprise a mixture of hydrogen and nitrogen gases. For example, the cooling of step (e) may be carried out for at least 5 minutes, e.g., for at least 6 minutes, for approximately 7.25 minutes, for no more than 10 minutes, and/or for no more than 8 minutes.

The bainitic microstructure of the shank portion provides toughness and durability, without brittleness. The martensitic microstructure of the working end portion provides hardness. The second steel composition of the working end portion, having a microstructure comprising martensite, may be tempered as required, to achieve the required hardness and durability (i.e. the required balance between hardness and brittleness).

According to a fifth aspect, a process of producing a steel chisel, comprises:

-   -   (a) providing a shank portion of the chisel formed from a first         steel composition selected from the group consisting of: 1.6582         34CrNiMo6; and 1.2249 45SiCrV6;     -   (b) providing a working end portion of the chisel formed from a         second steel composition selected from the group consisting of:         S7; 1.2357 50CrMoV 13-14; 1.2542 45WCrV7; and 1.2362×63CrMoV         5-1;     -   (c) joining together the shank portion and the working end         portion;     -   (d) heating the joined shank and working end portions to a         temperature of at least 730 degrees Celsius such that they both         have a microstructure comprising austenite; and     -   (e) cooling the heated joined shank and working end portions         such that the first steel composition of the shank portion         adopts a microstructure comprising bainite and such that the         second steel composition of the working end portion adopts a         microstructure comprising martensite.

Embodiments of this aspect may include one or more of the following features. Step (c) of the process according to the fifth aspect of the invention may comprise welding together the shank portion and the working end portion, e.g., friction welding together the shank portion and the working end portion. Step (d) of the process according to the fifth aspect of the invention may include heating the joined shank and working end portions to a temperature of, e.g., at least 750 degrees Celsius, at least 850 degrees Celsius, at least 950 degrees Celsius, or approximately 1050 degrees Celsius. The joined shank and working end portions may be heated to a temperature of no greater than 1200 degrees Celsius, e.g., greater than 1100 degrees Celsius. The heating of step (d) may be carried out for, e.g., at least 8 minutes, at least 12 minutes, or approximately 17 minutes.

Step (e) of the process according to the fifth aspect of the invention may comprise quenching (quench cooling), especially gas quenching, the joined shank and working end portions. The quench gas may comprise a mixture of hydrogen and nitrogen gases. The cooling of step (e) is carried out for at least 5 minutes, e.g., for at least 6 minutes, for example for approximately 7.25 minutes. The cooling of step (e) may be carried out for no more than 10 minutes, e.g., for no more than 8 minutes.

The bainitic microstructure of the shank portion provides toughness and durability, without brittleness. The martensitic microstructure of the working end portion provides hardness. The second steel composition of the working end portion, having a microstructure comprising martensite, may be tempered as required, to achieve the required hardness and durability (i.e. the required balance between hardness and brittleness).

The chisels of each of the first, second and third aspects of the invention may be produced by the process according to the fourth aspect of the invention or by the process according to the fifth aspect of the invention. The shank portion of the process provides the shank region of the chisel, and the working end portion of the process provides the working end region of the chisel.

The chisels according to this application may be chisel bits for use with power tools such as hammer drills or rotary hammers. The shank of the chisel at an opposite end region to the working end region may have a power tool attachment configuration, for example an “SDS” type of attachment configuration, for example, an SDS-PLUS or SDS-MAX attachment configuration.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows an embodiment of a point chisel;

FIG. 2 shows a detail of the point chisel of FIG. 1;

FIGS. 3( a) and 3(b) show further views of the point chisel of FIGS. 1 and 2;

FIG. 4 shows an embodiment of a flat chisel;

FIG. 5 shows a detail of the flat chisel of FIG. 4;

FIGS. 6( a) and 6(b) show further views of the flat chisel of FIGS. 4 and 5;

FIG. 7 shows a further detail of the flat chisel of FIGS. 4 to 6; and

FIG. 8 shows a cross-sectional view of the detail of FIG. 7.

FIG. 9 is a box plot showing data from comparative tests of depth of hole drilled.

FIG. 10 is a box plot showing data from comparative tests of chisel tip wear.

DETAILED DESCRIPTION OF THE DRAWINGS

FIGS. 1, 2 and 3 show an embodiment of a point chisel 1. FIG. 1 shows the entire chisel 1, FIG. 2 shows a detail of FIG. 1, FIG. 3( a) shows a front end view of the chisel 1, and FIG. 3( b) shows a side view of the detail of FIG. 2. The point chisel 1 includes a substantially circular cross-section shank 3 having a longitudinal axis 5. At one end of the shank 3 there is provided a known type of attachment configuration 27 for attaching the chisel to a hammer drill or rotary hammer. At the opposite end of the shank 3 a tapered working end region 7 is provided, in which the shank 3 tapers to a working point 9. The tapered working end region 7 comprises four converging substantially planar ribbed surfaces 11, each of which includes an elongate rib 13 protruding from the surface 11 and extending along the length of the surface. Adjacent ribbed surfaces 11 meet each other along part of their length at a substantially straight edge region 15 situated between adjacent elongate ribs 13. Each substantially straight edge region 15 projects radially outwardly with respect to the longitudinal axis 5.

The tapered working end region 7 includes a working point region 17 situated between the ribbed surfaces 11 and the working point 9. The working point region 17 comprises four converging substantially planar non-ribbed surfaces 19 which meet at the working point 9. Each non-ribbed surface 19 extends from a respective ribbed surface 11 but is not coplanar with it. The non-ribbed surfaces 19 converge at a greater angle than do the ribbed surfaces 11. Each rib 13 includes a front end surface 21 substantially coplanar with, and extending into, a respective non-ribbed surface 19 of the working point region 17. Each rib 13 has longitudinally extending substantially parallel and substantially planar side walls 23, and has a substantially constant width along its length. Additionally, each rib 13 varies in height along its length, above its respective ribbed surface, such that it includes an apex 25 situated part way along its length.

The shank 3 of the point chisel 1 is formed from steel having a microstructure comprising bainite, and the working end region 7 of the chisel 1 is formed from steel having a microstructure comprising martensite. The shank 3 and the working end region 7 have been welded together, by friction welding, and the weld joint is indicated at 29.

FIGS. 4 to 8 show an embodiment of a flat chisel 2 according to the invention. FIG. 4 shows the entire chisel 2, FIG. 5 shows a detail of FIG. 4, FIG. 6( a) shows a front end view of the chisel 2, FIG. 6( b) shows a side view of the detail of FIG. 5, FIG. 7 shows a perpendicular side view of the detail of FIG. 5, and FIG. 8 shows a cross-section X-X through the side view of FIG. 6. The flat chisel 2, which has a working edge 4, comprises a substantially cylindrical shank 6 having a longitudinal axis 8. At one end of the shank 6 there is provided a known type of attachment configuration 27 for attaching the chisel to a hammer drill or rotary hammer. At the opposite end of the shank 6 a working end region 10 is provided, comprising a pair of converging substantially planar ribbed surfaces 12 on opposite sides of the longitudinal axis 8. Each ribbed surface 12 extends directly from a cylindrical surface of the shank and includes three elongate ribs 14 a, 14 b and 14 c protruding from the surface and extending along part of the length of the surface. Each rib 14 has, along the majority of its length L, a substantially constant height H above the surface 12 from which it protrudes.

The ribs 14 of each ribbed surface 12 of the flat chisel 2 are substantially parallel to each other, and are parallel to a plane that extends through the longitudinal axis 8 and perpendicular to the ribbed surfaces 12. The central rib 14 b of each ribbed surface 12 is longer than the ribs 14 a and 14 c situated on each side of it. Each rib 14 has a substantially constant width W along its length L, and has a substantially flat upper surface 16, which is substantially parallel to the surface 12 from which the rib protrudes.

The working end region 10 of the flat chisel 2 includes a working edge region 18 situated between the ribbed surfaces 12 and the working edge 4. The working edge region 10 comprises a pair of converging substantially planar non-ribbed surfaces 20, each of which extends from a respective ribbed surface 12, which non-ribbed surfaces meet at the working edge 4. Each non-ribbed surface 20 is not coplanar with the ribbed surface 12 from which it extends, and the non-ribbed surfaces 20 converge at a greater angle than do the ribbed surfaces 12. Each rib 14 includes a front end surface 22 substantially coplanar with, and extending into, a respective non-ribbed surface 20 of the working edge region 18.

The working end region 10 of the flat chisel includes a widened portion 24 which is wider than the cylindrical shank 6, and which extends to the working edge 4. Two of the ribs 14 a, 14 c of each ribbed surface 12 extend along opposite lateral edges of the widened portion 24, such that respective side walls 26 of the two ribs form part of opposite lateral surfaces 28 defining the opposite lateral edges of the widened portion 24.

The shank 6 of the flat chisel 2 is formed from steel having a microstructure comprising bainite, and the working end region 10 of the chisel 2 is formed from steel having a microstructure comprising martensite. The shank 6 and the working end region 10 have been welded together, by friction welding, and the weld joint is indicated at 30.

Each of the chisel 1 and the chisel 2 may be formed using the following process steps:

(a) providing a shank portion of the chisel formed from a first steel composition;

(b) providing a working end portion of the chisel formed from a second steel composition, the second steel composition being different to the first steel composition;

(c) joining together the shank portion and the working end portion, for example by a welding operation, such as friction welding;

(d) heating the joined shank and working end portions such that they both have a microstructure comprising austenite; and

(e) cooling the heated joined shank and working end portions such that the first steel composition of the shank portion adopts a microstructure comprising bainite and such that the second steel composition of the working end portion adopts a microstructure comprising martensite.

Step (d) of the process may include heating the joined shank and working end portions to a temperature of at least 730 degrees Celsius, e.g., at least 750 degrees Celsius, at least 850 degrees Celsius, at least 950 degrees Celsius, or at least 1050 degrees Celsius. The joined shank and working end portions may be heated to a temperature no greater than 1200 degrees Celsius, e.g., no greater than 1100 degrees Celsius. The heating of step (d) may be carried out for at least 8 minutes, e.g., for at least 12 minutes, or for approximately 17.5 minutes.

Step (e) of the process may include quenching (quench cooling), e.g., gas quenching, the joined shank and working end portions. The quench gas may comprise a mixture of hydrogen and nitrogen gases. For example, the cooling of step (e) may be carried out for at least 5 minutes, e.g., for at least 6 minutes, for approximately 7.25 minutes, for no more than 10 minutes, and/or for no more than 8 minutes.

The steel of the working end region may be selected from the group consisting of: S7; 1.2357 50CrMoV 13-14; 1.2542 45WCrV7; and 1.2362 X63CrMoV 5-1. The steel of the shank may be selected from the group consisting of: 1.6582 34CrNiMo6; and 1.2249 45SiCrV6. The bainitic microstructure of the shank portion provides toughness and durability, without brittleness. The martensitic microstructure of the working end portion provides hardness. The second steel composition of the working end portion, having a microstructure comprising martensite, may be tempered as required, to achieve the required hardness and durability (i.e. the required balance between hardness and brittleness).

FIG. 9 is a box plot of the hole depth drilled during 15 seconds of operation, in B40 grade concrete using four different chisel samples. Data was collected from a range of chisels, in four sample sets, A, B, C and D. Sample sets A, B and C contained currently available point chisels from three different sources, not according to the invention. Sample set D contained point chisels of a shape and material according to relevant aspects of the invention. For each sample set, the depth of hole which could be drilled during 15 seconds of operation was measured for new chisels (A, B, C, D), and for chisels which had already been used for 240 minutes (A′, B′, C′, D′).

FIG. 9 shows that the speed of the chisels according to the invention is slightly lower than the speed of chisels in the comparative samples, when the chisels are new. However, the speed of chisels according to the invention which had already been used for 240 minutes was very good, especially in comparison to the chisels from sample sets A, B and C which had already been used for 240 minutes. Furthermore, the speed of the chisels according to the invention increased after the chisels had been used for 240 minutes, rather than decreasing as seen for the chisels from sample sets A, B and C. The improvement in speed with use is an advantage displayed by chisels according to the invention.

FIG. 10 is a box plot showing data from comparative tests of chisel tip wear after 4 hours of use. The sample sets A, B, C and D correspond to the same sample sets of FIG. 9. It can be seen that the tip wear after 4 hours of use was lower in the chisels of sample set D, which are chisels according to the invention. Lower tip wear is advantageous, since it results in longer life of the chisel. 

1. A point chisel, comprising: a substantially circular cross-section shank having a longitudinal axis; and a tapered working end region in which the shank tapers to a working point, the tapered working end region comprising at least three converging substantially planar ribbed surfaces, each of which includes an elongate rib protruding therefrom and extending along at least part of the length thereof, wherein adjacent ribbed surfaces meet each other along at least part of their length at a substantially straight edge region situated between adjacent elongate ribs.
 2. A chisel according to claim 1, wherein each substantially straight edge region projects radially outwardly with respect to the longitudinal axis.
 3. A chisel according to claim 1, wherein the tapered working end region includes a working point region situated between the ribbed surfaces and the working point, the working point region comprising at least three converging substantially planar non-ribbed surfaces which meet at the working point.
 4. A chisel according to claim 3, wherein each non-ribbed surface extends from a respective ribbed surface but is not coplanar therewith.
 5. A chisel according to claim 1, wherein each rib has longitudinally extending substantially parallel and substantially planar side walls.
 6. A chisel according to claim 1, wherein the adjacent ribbed surfaces comprise four converging substantially planar ribbed surfaces.
 7. A chisel according to claim 1, wherein the shank is composed of steel having a microstructure comprising bainite, and the working end region is composed of steel having a microstructure comprising martensite, wherein the shank and the working end region are welded together.
 8. A flat chisel comprising: a substantially cylindrical shank having a longitudinal axis; and a working end region comprising a pair of converging substantially planar ribbed surfaces on opposite sides of the longitudinal axis, each of which extends directly from a cylindrical surface of the shank and includes a plurality of elongate ribs protruding therefrom and extending along at least part of the length thereof, each rib having, along the majority of its length, a substantially constant height above the surface from which it protrudes.
 9. A chisel according to claim 8, wherein the ribs of each ribbed surface are substantially parallel to each other, and are substantially parallel to a plane that extends through the longitudinal axis and perpendicular to the ribbed surfaces.
 10. A chisel according to claim 8, wherein each ribbed surface has at least three ribs.
 11. A chisel according to claim 8, wherein at least one of the ribs of each ribbed surface is longer than the other rib or ribs.
 12. A chisel according to claim 11, wherein the ribs comprise a middle rib that is longer than side ribs situated on each side of the middle rib.
 13. A chisel according to claim 8, wherein the working end region includes a working edge region situated between the ribbed surfaces and the working edge, the working edge region comprising a pair of converging substantially planar non-ribbed surfaces, each of which extends from a respective ribbed surface, which non-ribbed surfaces meet at the working edge.
 14. A chisel according to claim 13, wherein each non-ribbed surface is not coplanar with the ribbed surface from which it extends.
 15. A chisel according to claim 8, wherein the shank is composed of steel having a microstructure comprising bainite, and the working end region is composed of steel having a microstructure comprising martensite, wherein the shank and the working end region are welded together.
 16. A steel chisel, comprising: an elongate shank having a longitudinal axis, and a working end region, wherein the steel of the shank has a microstructure comprising bainite, and the steel of the working end region has a microstructure comprising martensite.
 17. A chisel according to claim 16, wherein the shank and the working end region are welded together.
 18. A chisel according to claim 17, wherein the shank and the working end region are friction welded together.
 19. A chisel according to any claim 16, wherein the steel of the working end region includes one of S7; 1.2357 50CrMoV 13-14; 1.2542 45WCrV7; and 1.2362×63CrMoV 5-1, and the steel of the shank includes one of 1.6582 34CrNiMo6; and 1.2249 45SiCrV6.
 20. A process of producing a steel chisel, comprising: (a) forming a shank portion of a chisel from steel that includes one of 1.6582 34CrNiMo6; and 1.2249 45SiCrV6; (b) forming a working end portion of a chisel from steel that includes one of S7; 1.2357 50CrMoV 13-14; 1.2542 45WCrV7; and 1.2362×63CrMoV 5-1, (c) welding together the shank portion to the working end portion; (d) heating the welded shank and working end portions to a temperature of at least 730 degrees Celsius; and (e) allowing the heated welded shank and working end portions to cool, thereby causing the steel of the shank portion to adopt a microstructure comprising bainite and the steel of the working end portion to adopt a microstructure comprising martensite. 